LL 1001 为丁烯线型低密度聚乙烯吹膜树脂，具有良好的牵伸性。由 LL 1001 树脂制成的薄膜具有良好的拉伸性能和韧性。

LL 1001.32是一种丁烯线型低密度聚乙烯树脂。 由LL 1001.32制成的薄膜具有极佳的拉伸性能和韧性。

ExxonMobil™ LL 1001AV is an ethylene 1-butene linear low density polyethylene resin that offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001AV resin.

LL 1001AV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV stabilizer should be added to meet cable jacketing specifications. TnPP is not intentionally added to LL 1001AV resin.

ExxonMobil™ LL 1001BT resin offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001BT resin.

ExxonMobil™ LL 1001BU resin offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1001BU resin.

LL 1002系列为丁烯线型低密度聚乙烯，为吹膜加工而开发，具有高光泽和卓越的牵伸性能。 由LL1002 树脂制成的薄膜具有极佳的拉伸性能和韧性。

LL 1002AY is a butene LLDPE designed for the blown film process, offering high gloss and excellent draw down. Films made from LL1002AY have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002AY.

LL 1002AY is an LLDPE resin designed for cast films. It offers high gloss and excellent drawdown in both blown and cast film applications. LL 1002AY may also be used as a blend partner with LDPE resins to improve film properties and processability. TnPP is not intentionally added to LL 1002AY resin.

LL 1002AY is a C4 Ziegler Natta LLDPE for Low Voltage power cable and Telecom jacketing. The grade contains a higher level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV stabilizer should be added to meet cable jacketing specifications. TnPP is not intentionally added to LL 1002AY resin.

ExxonMobil™ LL 1002BU resin is an ethylene 1-butene linear low density polyethylene designed for the blown film process. It offers high gloss and excellent draw down. Films made from LL 1002BU have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002BU resin.

ExxonMobil™ LL 1002xBU resin is an ethylene 1-butene linear low density polyethylene designed for the blown film process. It offers high gloss and excellent draw down. Films made from LL 1002xBU have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002xBU resin.

LL 1002YB是一种用于低压电缆和电信护套的C4齐格勒-纳塔线型低密度聚乙烯。 该牌号抗氧化剂含量较高，并具有卓越的耐环境应力开裂性。 应添加炭黑或紫外线稳定剂以使产品符合电缆护套规范。

LL 1004AY is an LLDPE grade, offering excellent high temperature stability. Properties may be further enhanced by combining with Exceed™ mLLDPE. TnPP is not intentionally added to LL 1004AY resin.

LL 1004AY is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements for insulation. For jacketing applications, addition of Carbon Black or UV stabilizer is required. TnPP is not intentionally added to LL 1004AY resin.

LL 1107 树脂为小数熔融指数丁烯线型低密度聚乙烯吹膜树脂。 由LL 1107树脂制成的薄膜具有良好的挺度和拉伸强度。 这些树脂的强度和牵伸性使其在多种薄膜用途中都有出色的表现。

LL 1201系列为线型低密度聚乙烯牌号，良好地结合了硬度和光学性能（与10-20%的低密度聚乙烯结合）

LL 1201AV is a LLDPE grade, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE). TnPP is not intentionally added to LL 1201AV.

LL 1201BS is a LLDPE grade, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE). TnPP is not intentionally added to LL 1201BS.

LL 1236 树脂为具有强化挺度的丁烯线型低密度聚乙烯。 它们可单独或作为一种成分用于包装膜和工业膜。

LL 3001.32是一种乙烷共聚物线型低密度聚乙烯，为吹塑或流延膜加工而开发。 由LL 3001.32制成的薄膜具有卓越的拉伸性能和韧性。 卓越的强度性能连同良好的拉拔性使其成为多用途包装膜树脂。

ExxonMobil™ LL 3001.63 is an ethylene 1-hexene linear low density polyethylene resin formulated for blown film extrusion. Films made from this resin have outstanding tensile and toughness properties. Superior strength properties, along with excellent drawability, make this a very versatile packaging film resin.

LL 3002.32 is a hexene copolymer LLDPE cast film resin. Films made from LL 3002.32 resin have outstanding tensile and toughness properties. These superior properties, along with the excellent drawability, make it a versatile packaging film resin.

LL 3003 树脂为乙烷共聚物线型低密度聚乙烯流延膜树脂。 由LL 3003 树脂制成的薄膜具有卓越的拉伸性能和硬度及韧性。 这些树脂卓越的性能连同良好的拉拔性使其成为多用途包装膜树脂。

LL 3201 树脂为己烯共聚物线性低密度聚乙烯薄膜树脂。 由LL 3201树脂制成的薄膜具有卓越的拉伸性能、硬度和韧性。 这些卓越的性能连同良好的牵伸性使其可用于要求严格的包装用途。

ExxonMobil™ LL 3402.48 is an ethylene 1-hexene medium density polyethylene blown film resin for applications requiring high stiffness. It can also be used in cast films. Films produced from this resin exhibit good tensile and puncture resistance properties.

LL 3402.48是一种乙烷中等密度聚乙烯流延膜牌号，用于高强度和高硬度要求的用途。 它还可用于吹膜。 由该树脂制成的薄膜具有良好的拉伸性能和抗穿刺性能。

LL 3404.48是一种乙烷中等密度聚乙烯流延膜牌号，用于高强度和高硬度要求的用途。 由该树脂制成的薄膜具有良好的拉伸性和抗穿刺性

ExxonMobil™ LL 4004AZ is an ethylene 1-butene Ziegler Natta linear low density polyethylene resin especially designed for Low Voltage power cable insulation using either the one-step or two-step silane cross-linking process. Sufficient antioxidant and Cu inhibitor should be added to meet specific ageing requirements.

埃克森美孚LL 5002.09是一种线性低密度聚乙烯树脂，具有良好的加工性和简易的混合性。 LL 5002.09 同样具有良好的韧性和耐环境应力开裂性。

埃克森美孚LL 5100.09是一种线性低密度聚乙烯树脂，具有良好的加工性和简易的混合性。 LL 5100.09 的颗粒形态使其可以有效地与色料、开口剂和爽滑剂混合

埃克森美孚LL 5252.09是一种线性低密度聚乙烯树脂，具有良好的加工性和简易的混合性。 LL 5252.09的颗粒形态使其可以有效地与色料、助滑和开口剂添加剂混合

LL 6100是一种具有窄分子量分布的丁烯共聚物，它使为有易加工性要求的用途而开发。 该树脂具有适合低温食品包装用途的卓越韧性和抗撕裂性。

LL 6101系列为具有中等流动性的线型低密度聚乙烯牌号，具有卓越的硬度、耐热变形性和良好的耐环境应力开裂性。 LL 6101 牌号卓越的韧性和耐环境应力开裂性使其成为高密度聚乙烯卓越的混料，其中它可提高桶和盖子之类的耐环境应力开裂性。

LL 6101 树脂为C4 齐格勒-纳塔线型低密度聚乙烯，推荐用于多种造粒用途。

LL 6201系列为高流动性线型低密度聚乙烯牌号，具有独特的卓越加工性和良好生产性能的组合。 与低密度聚乙烯产品相比，由LL 6201制成的部件具有良好的光泽并具有韧性、耐环境应力开裂性、硬度和耐热变形性方面的优势。

LL 6201 树脂为C4 齐格勒-纳塔线型低密度聚乙烯，推荐用于多种造粒用途。

LL 6201是一种具有窄分子量分布的丁烯共聚物，为具有易加工性高要求的薄壁部件而开发。 该树脂具有适用于冷冻食品包装用途的韧性和抗撕性而开发。

LL 6202是一种具有窄分子量分布的丁烯共聚物，为有卓越韧性的用途而开发。 该树脂具有适用于要求高抗撕裂性和低翘曲性用途的易加工性。

LL 6301系列为中等密度的线型低密度聚乙烯牌号，具有相对较高的分子量，使成型的物品更坚韧并具有卓越的耐环境应力开裂性。 与具有相似密度的低密度聚乙烯牌号相比，LL 6301 牌号具有较高的热变形温度和更高的耐长期蠕变性。