Texin® 393AE
Texin 393AE resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 93A/51D. It is processed primarily by extrusion but can also be used for injection molding.
Properties / Applications:
Texin 393AE resin is characterized by a low gel content, very good hydrolysis resistance, good abrasion resistance and very good chemical resistance to oils, solvents and other non-aqueous solutions. Typical applications include cable jackets, hose jackets and extruded profile. As with any product, use of Texin 393AE resin in a given application must be tested (including field testing,
etc.) in advance by the user to determine suitability.
Properties / Applications:
Texin 393AE resin is characterized by a low gel content, very good hydrolysis resistance, good abrasion resistance and very good chemical resistance to oils, solvents and other non-aqueous solutions. Typical applications include cable jackets, hose jackets and extruded profile. As with any product, use of Texin 393AE resin in a given application must be tested (including field testing,
etc.) in advance by the user to determine suitability.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Texin® 393AE 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Technical Datasheet (English)
下载文档可用性
北美洲, 欧洲
用途
Jacketing
加工方式
挤出
其他属性
特性, 密度 / 比重, 密度, 流动方向收缩, 垂直流动方向的收缩, 收缩率, 弯曲模量, 弯曲模量, 泰伯耐磨性, 拉伸应力（在100％时）, 拉伸应力（在100％时）, 300%时拉伸应力, 300%时拉伸应力, 抗张强度, 拉伸断裂应力, 断裂伸长率, 拉伸断裂应变, 撕裂强度, 撕裂强度, 压缩永久变形, 压缩永久变形, 巴肖氏弹性, 肖氏硬度, 肖氏硬度, 玻璃转化温度, 维卡软化温度, 维卡软化温度, 干燥温度, 干燥时间, 建议的最大水分含量, 建议的最大回制料比例, 料筒后部温度, 料筒中部温度, 料筒前部温度, 射嘴温度, 加工（熔体）温度, 模具温度, 注塑压力, 注射速度, 背压, 螺杆转速, 垫层, 干燥温度, 干燥时间, 建议的最大水分含量, 建议的最大回制料比例, 料筒1区温度, 料筒2区温度, 料筒3区温度, 熔体温度, 口模温度