Bioblend BT grades are developed for soft and flexible injection molded application. The grades are naturally high heat-stable at temperatures up to 95°C. Bioblend BT grades are biodegradable in all conditions. - injection molding grade - biopolymer compound, mineral filled - can be blended with bamboo powder (B), rice husk (R), coffee husk (C), wheat straw (W) and wood powder (H) - balanced flexibility to rigidity, good impact properties - naturally heat-stable up to 95°C - biodegradable in controlled (e.g. industrial compost) und non-controlled conditions (e.g. landfill, soil, roadside) - easy to process / easy to eject - food contact safe - dishwasher-ok, microwave-ok - global availability Bioblend BT25S (B/R/C/W/H) HH is a bio-polymer polymerized of succinic acid and 1,4-butanediol. The compound is enhanced with a blend of natural mineral and organic fillers. The material can additionally be blended with bamboo powder, rice husk or coffee husk to support a natural look. Bioblend BT25S (B/R/C/W/H) HH is designed to be completely biodegradable & compostable (microbial and enzymatic degradation) in the targeted disposal environment; it is biodegradable both in controlled (e.g. industrial compost factilities) and in non-controlled (e.g. soil, roadside, landfill) conditions. The grade offers a significant reduction in carbon footprint compared to traditional fossil-based plastics. The material has got balanced stiffness values with good impact properties. Bioblend BT25S (B/R/C) HH offers a very good processability and flow with an easy ejection of parts from the mould. Cycle times can be kept short. Part wall-thickness shall be greater than 1.2 mm.

Bioblend LT grades (optimized cPLA grade) are developed for rigid injection molded applications. The grades can be crystallized/annealed in order to have the part heat-stable at temperatures up to 110°C. Bioblend LT grades are biodegradable in controlled conditions. - injection molding grade - biopolymer compound, mineral filled - can be blended with bamboo powder (B), rice husk (R), coffee husk (C), wheat straw (W) and wood powder (H) - high rigidity - can be crystallized/annealed to be heatstable up to 110°C - biodegradable in controlled conditions (e.g. industrial compost) according to DIN EN 13432 / ASTM D6400 - easier to process than virgin PLA/cPLA - food contact safe - dishwasher-ok / microwave-ok - global availability Bioblend LT25B (B/R/C/W/H) is a modified PLA-blend. The grade is enhanced with a blend of natural mineral fillers. Bioblend LT grades are easy to process and prepared for a fast and efficient postprocessing crystallization/annealing process. The material can additionally be blended with bamboo powder, rice husk or coffee husk, wheat straw and wood powder to support a natural look. Bioblend LT25B (B/R/C/W/H) is compostable/biodegradable (microbial and enzymatic degradation) in the targeted disposal environment; it is biodegradable in controlled (e.g. industrial compost facilities) conditions according to EN 13432 (for Europe) and ASTM D6400 (for the USA). Bioblend LT grades offer a significant reduction in carbon footprint compared to fossil-based plastics. The grades exhibit excellent strength and stiffness properties as well as a good flow combined with improved elongation values. An increased rate of crystallization allows an annealing to a heat-stable temperature of 110 °C (HDT-B) and above. Part wall-thickness shall be greater than 1.5 mm.