DINALEN® 20 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 20 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 20 is extruded at recommended melt temperature range between 175°C and 200°C. Recommended film thickness: 0.050 mm to 0.200 mm.

DINALEN® 30 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 30 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 30 is extruded at recommended melt temperature range between 165°C and 185°C. Recommended film thickness: 0.030 mm to 0.100 mm.

DINALEN® 35 is low density polyethylene containing additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 35 exhibits excellent very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 35 is extruded at recommended melt temperature range between 165°C and 185°C. Recommended film thickness: 0.030 mm to 0.100 mm.

DINALEN 50 is low density polyethylene containing no additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent. DINALEN 50 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN 50 is extruded at recommended melt temperature range between 160°C and 180° C. Recommended film thickness: 0.025 to 0.060 mm. Application - Thin non-slippery film of high gloss and transparency - Heat shrinkable film with excellent stiffness for industrial bundling - Extruded foams with physical blowing agent - Small diameter pipe extrusion - Wire and cable sheathing - Injection moulded thick-walled products - Blown packaging and other shallow objects - Mixing and co-extrusion with suitable polyolefin grades

DINALEN® 55 is low density polyethylene containing slip and anti-blocking additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 55 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 55 is extruded at recommended melt temperature range between 160°C and 180°C. Recommended film thickness: 0.25 to 0.05mm. Application - Thin slippery film of high gloss and transparency - Production of film for lamination - Production of film for a variety of primary flexible packaging like FFS for foodstuffs, sanitary articles, chemicals - Film production for a many kinds of carrier-bags, like airport security bags, DTK bags, cooler-bags, T-shirt-bags, shoulder-bags - Blending with DINALEN 50 to obtain a less slippery film - Mixing and co-extrusion with suitable i-polybutene-1 grades to produce film for peel systems - Mixing and co-extrusion with suitable polyolefin grades

DINALEN® 65 is low density polyethylene containing slip and anti-blocking additives. It is intended for thin blow film extrusion. Other processing techniques can be used in less extent. DINALEN® 65 exhibits excellent processability, uniform optical and other properties, depending on its application. It is extruded at temperatures ranging from 140°C to 165°C. DINALEN® 65 gives films of desired properties depending on selected processing parameters such as processing temperature and capacity; blowing ratio, and the height of the frost line. Recommended film thickness : 0.020 mm to 0.040 mm.