Commercial: Active

E121562 - SABIC INNOVATIVE PLASTICS US L L C

Descargar documento

E121562 - SABIC INNOVATIVE PLASTICS US L L C

Descargar documento

Latin America, North America

Additive Manufacturing (3D Printing)

CHRYSLER MS-DB-200 Type A CPN2877 Color: 90% Color Match

• Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
• Flexural DMA (ASTM D5023)
• Shear DMA (ASTM D4065)
• Specific Heat vs. Temperature (ASTM E1269)
• Specific Volume vs. Temperature (PVT)
• Tensile Creep (ASTM D2990)
• Tensile Fatigue
• Tensile Stress vs. Strain (ASTM D638)
• Thermal Conductivity vs. Temperature (ASTM E1530)
• Viscosity vs. Shear Rate (ASTM D3835)

Also Available In, Density / Specific Gravity, Density, Melt Mass-Flow Rate (MFR), Melt Mass-Flow Rate (MFR), Molding Shrinkage, Tensile Modulus, Tensile Modulus, Tensile Strength at Yield, Tensile Stress at Yield, Tensile Strength at Break, Tensile Stress at Break, Tensile Elongation at Yield, Tensile Strain at Yield, Tensile Elongation at Break, Tensile Strain at Break, Flexural Modulus, Flexural Modulus, Flexural Stress, Flexural Strength at Yield, Charpy Notched Impact Strength, Notched Izod Impact, Notched Izod Impact Strength, Instrumented Dart Impact, Rockwell Hardness, DTUL (66 psi) - Unannealed, DTUL (264 psi) - Unannealed, DTUL (1.80 MPa) Unannealed, Vicat Softening Temperature, Vicat Softening Temperature, CLTE, Flow (TMA), CLTE, Transverse (TMA), RTI Elec, RTI Imp, RTI Str, Arc Resistance, Comparative Tracking Index (CTI), High Amp Arc Ignition (HAI), High Voltage Arc Resistance to Ignition (HVAR), Hot-wire Ignition (HWI), Flame Rating, Melt Viscosity, Drying Temperature, Drying Time, Suggested Max Moisture, Suggested Shot Size, Rear Temperature, Middle Temperature, Front Temperature, Nozzle Temperature, Processing (Melt) Temp, Mold Temperature, Back Pressure, Screw Speed, Vent Depth, Injection Notes