| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic XLPE
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
0.907 to 0.976
|
|
ASTM D792 |
|
73°F
|
0.922 to 1.14
|
g/cm³
|
ISO 1183 |
|
--
|
0.917 to 0.954
|
g/cm³
|
ASTM D1505 |
|
Apparent Density
|
0.47 to 1.26
|
g/cm³
|
ASTM D1895 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
190°C/2.16 kg
|
0.32 to 3.5
|
g/10 min
|
ASTM D1238 |
|
190°C/2.16 kg
|
0.93 to 2.2
|
g/10 min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
|||
|
Yield, 73°F
|
2290 to 4500
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
2170 to 3210
|
psi
|
ISO 527-2 |
|
73°F
|
2440 to 2900
|
psi
|
ASTM D638 |
|
73°F
|
1450 to 2030
|
psi
|
ISO 527-2 |
|
Tensile Elongation
|
|||
|
Break, 73°F
|
340 to 520
|
%
|
ASTM D638 |
|
Break, 73°F
|
140 to 460
|
%
|
ISO 527-2 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield, 73°F)
|
1670 to 2400
|
psi
|
ASTM D412 |
|
Tensile Elongation (Break, 73°F)
|
160 to 300
|
%
|
ASTM D412 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
73°F
|
50 to 60
|
|
ASTM D2240 |
|
73°F
|
52 to 56
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Brittleness Temperature
|
-111 to -102
|
°F
|
ASTM D746 |
|
Vicat Softening Temperature
|
246 to 261
|
°F
|
ASTM D1525 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity
|
|||
|
73°F
|
1.0E+2 to 1.0E+16
|
ohm·cm
|
ASTM D257 |
|
73°F
|
10 to 1.1E+16
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|||
|
73°F
|
510 to 1200
|
V/mil
|
ASTM D149 |
|
73°F
|
550 to 570
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|||
|
73°F
|
2.30 to 3.70
|
|
ASTM D150 |
|
73°F
|
2.29 to 2.31
|
|
IEC 60250 |
|
Dissipation Factor
|
|||
|
73°F
|
0.00030 to 0.010
|
|
ASTM D150 |
|
73°F
|
0.00030 to 0.00051
|
|
IEC 60250 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Oxygen Index
|
|||
|
--
|
25 to 27
|
%
|
ASTM D2863 |
|
--
|
26 to 36
|
%
|
ISO 4589-2 |
| Extrusion |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
139 to 140
|
°F
|
|
|
Drying Time
|
4.0 to 5.2
|
hr
|
|
|
Cylinder Zone 1 Temp.
|
264 to 347
|
°F
|
|
|
Cylinder Zone 2 Temp.
|
281 to 365
|
°F
|
|
|
Cylinder Zone 3 Temp.
|
291 to 375
|
°F
|
|
|
Cylinder Zone 4 Temp.
|
302 to 402
|
°F
|
|
|
Cylinder Zone 5 Temp.
|
343 to 405
|
°F
|
|
|
Melt Temperature
|
264 to 277
|
°F
|
|
|
Die Temperature
|
317 to 411
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic XLPE
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |