| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic PE Copolymer
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
0.869 to 0.965
|
|
ASTM D792 |
|
73°F
|
0.939 to 0.974
|
g/cm³
|
ISO 1183 |
|
--
|
0.931 to 1.30
|
g/cm³
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
190°C/2.16 kg
|
0.97 to 25
|
g/10 min
|
ASTM D1238 |
|
190°C/2.16 kg
|
0.070 to 2.1
|
g/10 min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (73°F)
|
2470 to 93500
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|||
|
Yield, 73°F
|
3010 to 4250
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
2860 to 3770
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
933 to 5370
|
psi
|
ISO 527-2 |
|
Tensile Strain
|
|||
|
Yield, 73°F
|
8.9 to 11
|
%
|
ISO 527-2 |
|
Break, 73°F
|
200 to 1000
|
%
|
ASTM D638 |
|
Break, 73°F
|
510 to 970
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|||
|
73°F
|
12500 to 143000
|
psi
|
ASTM D790 |
|
73°F
|
2610 to 168000
|
psi
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
4.7 to 6.3
|
ft·lb/in²
|
ISO 179 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness
|
|||
|
73°F
|
30 to 93
|
|
ASTM D2240 |
|
73°F
|
55 to 62
|
|
ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Vicat Softening Temperature
|
|||
|
--
|
236 to 240
|
°F
|
ASTM D1525 |
|
--
|
253 to 257
|
°F
|
ISO 306 |
|
Melting Temperature (DSC)
|
186 to 226
|
°F
|
ISO 3146 |
| Notes |
| 1Typical properties: these are not to be construed as specifications. |