| Product Description | ||||
|
This data represents typical values that have been calculated from all products classified as: Generic EPE
This information is provided for comparative purposes only. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
0.917 to 0.920
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
0.80 to 1.2
|
g/10 min
|
ASTM D1238 |
| Films |
Nominal Value
|
Unit
|
Test Method
|
|
Film Thickness - Tested
|
0.79 to 2.0
|
mil
|
|
|
Film Puncture Energy
|
49.5
|
in·lb
|
|
|
Film Puncture Force
|
9.84 to 21.9
|
lbf
|
|
|
Film Puncture Resistance
|
228
|
ft·lb/in³
|
|
|
Secant Modulus
|
ASTM D882 | ||
|
MD
|
10000 to 40600
|
psi
|
|
|
TD
|
11200 to 52100
|
psi
|
|
|
Tensile Strength
|
ASTM D882 | ||
|
MD: Yield
|
850 to 2070
|
psi
|
|
|
TD: Yield
|
1160 to 2150
|
psi
|
|
|
MD: Break
|
5760 to 8340
|
psi
|
|
|
TD: Break
|
5220 to 7540
|
psi
|
|
|
Tensile Elongation
|
ASTM D882 | ||
|
MD: Break
|
390 to 600
|
%
|
|
|
TD: Break
|
500 to 730
|
%
|
|
|
Dart Drop Impact (73°F)
|
310 to 1000
|
g
|
ASTM D1709 |
|
Elmendorf Tear Strength
|
ASTM D1922 | ||
|
MD
|
240 to 570
|
g
|
|
|
TD
|
420 to 1100
|
g
|
|
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Vicat Softening Temperature
|
187 to 266
|
°F
|
ASTM D1525 |
|
Melting Temperature (DSC)
|
251 to 255
|
°F
|
ISO 3146 |
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Gloss
|
32 to 96
|
|
ASTM D2457 |
|
Haze
|
0.50 to 20
|
%
|
ASTM D1003 |
| Extrusion |
Nominal Value
|
Unit
|
|
|
Melt Temperature
|
420 to 521
|
°F
|
|
| Extrusion Notes | |||
|
This data represents typical values that have been calculated from all products classified as: Generic EPE
This information is provided for comparative purposes only. |
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |