| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Agency Ratings
|
|
|||
|
RoHS Compliance
|
|
|||
|
Appearance
|
|
|||
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress
|
|||
|
100% Strain
|
|
psi
|
ASTM D412 |
|
100% Strain, 0.0748 in
|
|
psi
|
ISO 37 |
|
Tensile Strength (Break, 0.0748 in)
|
|
psi
|
ASTM D412, ISO 37 |
|
Tensile Elongation
|
|||
|
Break
|
|
%
|
ASTM D412 |
|
Break, 0.0748 in
|
|
%
|
ISO 37 |
|
Tear Strength 2 (75°F)
|
|
lbf/in
|
ASTM D624 |
|
Compression Set
|
ASTM D395, ISO 815 | ||
|
75°F, 22.0 hr
|
|
%
|
|
|
212°F, 22.0 hr
|
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness (Shore A, 0.0748 in, Compression Molded)
|
|
|
ASTM D2240, ISO 868 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Brittleness Temperature
|
|
°F
|
ASTM D746, ISO 812 |
| Additional Information | |||
|
The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.
The value listed as Density, ISO 1183, was tested in accordance with ISO 2781. The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48. Permanent Set (Tension), ASTM D412, Compression Molding, 1.9 mm: 17% 100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 122% Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 117% Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 107% Hardness, ISO 48, Physical Retention After 7 Days at 125°C, Shore A, Compression Molding, 1.9 mm: 74 Viscosity, ASTM D3835, 300 s-1 at 190°C, Compression Molding, 1.9 mm: 455 Pa*s Typical Processing Temperature, Compression Molding, 1.9 mm: 177° C Volume Change, ASTM D471, ISO 1817, After 7 days, 100°C, Water, Compression Molding, 1.9 mm: 14% Volume Change, After 7 days,ASTM D471, ISO 1817, 24°C, Fuel B, Compression Molding, 1.9 mm: 24% Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, ASTM #1 Oil, Compression Molding, 1.9 mm: -7% Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, IRM 903 Oil #3, Compression Molding, 1.9 mm: 13% Clash-Berg Stiffness Temperature, ASTM D1043, 10000 psi, Compression Molding, 1.9 mm: -22° C |
|||
| Related Terminology | |||
|
This supplier and product may also be known by these terms: APA, Advanced Polymer Alloys is a division of FerroProduct names can be difficult to match. You may have searched any one of these terms to find this product: Alcryn® 2180 NC, Alcryn 2180 NC, Alcryn® , Alcryn, Alcryn2180NC, 2180 NC, 2180NC, Melt Processable Rubber, MPR, Thermoplastic Elastomer, TPE, APA, MeltProcessableRubber, ThermoplasticElastomer, NC2180
|
|||
| Features | |||
|
Features may also be described by the following terms: Good Abrasion Resistance, Abrasion Resistant, Good Chemical Resistance, Chemical Resistant, High Flow, High Melt, High MFI, High Friction, Good Tear Strength.
|
|||
| Uses | |||
|
Uses may also be described by the following terms: Tubing, Tube.
|
|||
| Agency Ratings | |||
|
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): EU (1).
|
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2Die C |
|
UL and the UL logo are trademarks of UL LLC © 2013. All Rights Reserved.
The information presented on this datasheet was acquired by UL IDES from the producer of the material. UL IDES makes substantial efforts to assure the accuracy of this data. However, UL IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. |