| General | |
|
Material Status
|
|
|
Availability
|
|
|
Features
|
|
|
Appearance
|
|
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
| Elastomers |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress (100% Strain)
|
|
psi
|
ASTM D412 |
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D412 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D412 |
|
Tear Strength
|
|
lbf/in
|
ASTM D624 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Durometer Hardness (Shore A)
|
|
|
ASTM D2240 |
| Thermoset |
Nominal Value
|
Unit
|
Test Method
|
|
Post Cure Time (302°F)
|
|
hr
|
|
| Additional Information | |||
|
Compression Set, ASTM D395, 22 hr, 302°F, Specimen post-cured 1 hr at 302°F: 29%
Compression Set, ASTM D395, 22 hr, 302°F, Specimen post-cured 4 hrs at 392°F: 5% Viscosity, Part A: 1000 Pa.s Viscosity, Part B: 1000 Pa.s Cure Rate, ODR, 302°F, T10: 20 sec Cure Rate, ODR, 302°F, T90: 30 sec Press Cure, 5 min at 248°F |
|||
| Related Terminology | |||
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Shincor LIM KE2001-50, Shincor LIM KE200150, Shincor LIM , ShincorLIMKE200150, ShincorLIM, KE 2001, LIMKE 2001 50, LIMKE 2001, LIMKE2001-50, LIMKE200150, LIMKE2001:50, LIMKE2001/50, LIMKE2001+50, LIMKE2001_50, LIMKE2001 50, LIMKE2001, KE 2001 50, KE2001-50, KE200150, KE2001:50, KE2001/50, KE2001+50, KE2001_50, KE2001 50, KE2001, 200150, Silicone, Shincor Sil, 2001KE, 2001LIMKE
|
|||
| Features | |||
|
Features may also be described by the following terms: Fast Cure, Fast Curing.
|
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
|
UL and the UL logo are trademarks of UL LLC © 2013. All Rights Reserved.
The information presented on this datasheet was acquired by UL IDES from the producer of the material. UL IDES makes substantial efforts to assure the accuracy of this data. However, UL IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. |