| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ISO 1133 | ||
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/1 |
|
Tensile Stress
|
ISO 527-2/1BA/50 | ||
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Tensile Creep Modulus
|
ISO 899-1 | ||
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact Strength
|
ISO 180/1A | ||
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Tensile Impact Strength
|
|
ft·lb/in²
|
ISO 8256/1B |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Ball Indentation Hardness (H 132/30)
|
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
| Additional Information | |||
|
Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >500%
ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 40hr Tensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.6% Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 34 MPa Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 131°C Enthalpy Change, DIN 53765: 206J/g |
|||
| Related Terminology | |||
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® Vestolen A 5017, SABIC Vestolen A 5017, SABIC® Vestolen A , SABIC Vestolen A, SABICVestolenA5017, SABICVestolenA, A 5017, A5017, 5017, Polyethylene, High Density, Polyethylene High Density, HDPE, Polyethylene, PE, SABIC, PolyethyleneHighDensity, 5017A
|
|||
| Features | |||
|
Features may also be described by the following terms: High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant, Narrow Molecular Weight Distribution, Narrow MW Distribution, Good Processability, Easy Processing, Low Warpage, Low Warp, Good Toughness, Tough, High Purity.
|
|||
| Uses | |||
|
Uses may also be described by the following terms: Closure Caps, Caps, Cap.
|
|||
| Agency Ratings | |||
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
|
UL and the UL logo are trademarks of UL LLC © 2013. All Rights Reserved.
The information presented on this datasheet was acquired by UL IDES from the producer of the material. UL IDES makes substantial efforts to assure the accuracy of this data. However, UL IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. |