| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
RoHS Compliance
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
|||
|
--
|
|
|
ASTM D792 |
|
73°F
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
ASTM D1238 | ||
|
200°C/5.0 kg
|
|
g/10 min
|
|
|
220°C/10.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
|
in³/10min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Stress
|
|||
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break
|
|
psi
|
ISO 527-2/50 |
|
0.118 in 2
|
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|||
|
Break, 0.118 in 2
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
0.236 in 3
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|||
|
0.236 in 3
|
|
psi
|
ASTM D790 |
|
-- 4
|
|
psi
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179 |
|
Notched Izod Impact
|
|||
|
73°F, 0.118 in
|
|
ft·lb/in
|
ASTM D256 |
|
73°F, 0.236 in
|
|
ft·lb/in
|
ASTM D256 |
|
--
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength
|
|
ft·lb/in²
|
ISO 180/1U |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
264 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
|
°F
|
ASTM D648 |
|
264 psi, Annealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|||
|
--
|
|
°F
|
ASTM D1525 5 |
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (0.0630 in)
|
|
|
UL 94 |
| Related Terminology | |||
|
This supplier and product may also be known by these terms: ChiMeiProduct names can be difficult to match. You may have searched any one of these terms to find this product: POLYLAC® PA-707, POLYLAC PA707, POLYLAC® , POLYLAC, POLYLACPA707, PA, PA-707, PA707, PA:707, PA/707, PA+707, PA_707, PA 707, Acrylonitrile Butadiene Styrene, ABS, Chi Mei, AcrylonitrileButadieneStyrene, 707PA
|
|||
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
|
°F
|
|
|
Drying Time
|
|
hr
|
|
|
Rear Temperature
|
|
°F
|
|
|
Middle Temperature
|
|
°F
|
|
|
Front Temperature
|
|
°F
|
|
|
Mold Temperature
|
|
°F
|
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 20.24 in/min |
| 30.11 in/min |
| 40.079 in/min |
| 5Rate A (50°C/h) |
|
UL and the UL logo are trademarks of UL LLC © 2013. All Rights Reserved.
The information presented on this datasheet was acquired by UL IDES from the producer of the material. UL IDES makes substantial efforts to assure the accuracy of this data. However, UL IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. |