| Product Description | ||||
|
Compound based on Polyamide 12 (PA 12).
Glass fibres. |
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage 2
|
ISO 294-4 | ||
|
Across Flow: 0.0787 in
|
|
%
|
|
|
Flow: 0.0787 in
|
|
%
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
ISO 527-2/1 | ||
|
73°F
|
|
psi
|
|
|
140°F
|
|
psi
|
|
|
194°F
|
|
psi
|
|
|
248°F
|
|
psi
|
|
|
302°F
|
|
psi
|
|
|
Tensile Stress
|
ISO 527-2/5 | ||
|
Break, 73°F
|
|
psi
|
|
|
Break, 140°F
|
|
psi
|
|
|
Break, 194°F
|
|
psi
|
|
|
Break, 248°F
|
|
psi
|
|
|
Break, 302°F
|
|
psi
|
|
|
Tensile Strain
|
ISO 527-2/5 | ||
|
Yield, 73°F
|
|
%
|
|
|
Break, 73°F
|
|
%
|
|
|
Break, 140°F
|
|
%
|
|
|
Break, 194°F
|
|
%
|
|
|
Break, 248°F
|
|
%
|
|
|
Break, 302°F
|
|
%
|
|
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179/1eU |
|
Notched Izod Impact (73°F, 0.126 in)
|
|
ft·lb/in
|
ASTM D256A |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
|||
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50 |
|
CLTE - Flow (86 to 212°F)
|
|
in/in/°F
|
ASTM D696 |
|
Continuous Use Temperature 3
|
|
°F
|
|
| Related Terminology | |||
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Latamid 12 G/50, Latamid 12 G50, Latamid , Latamid12G50, 12 G, 12 G/50, 12 G50, 12 G:50, 12 G+50, 12 G-50, 12 G_50, 12 G 50, 12G, G50, 12G50, 12G_50, Polyamide 12, Nylon 12, Polyamide, Nylon, pa12, Lati, Polyamide12, Nylon12, G12
|
|||
| Generic Name | |||
|
Generic Name may also be described by the following terms: PA12.
|
|||
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
|
°F
|
|
|
Drying Time
|
|
hr
|
|
|
Processing (Melt) Temp
|
|
°F
|
|
|
Mold Temperature
|
|
°F
|
|
|
Injection Rate
|
|
|
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2at 60 MPa of cavity pressure |
| 320000 hr |
|
UL and the UL logo are trademarks of UL LLC © 2013. All Rights Reserved.
The information presented on this datasheet was acquired by UL IDES from the producer of the material. UL IDES makes substantial efforts to assure the accuracy of this data. However, UL IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier. |